Energy
- Bitumen
- Fuels
- Other Refinery Products
- Petrochemicals
- Toluene
- Triethylene Glycol
- Polyvinyl Chloride (PVC)
- C5
- Purified Terepthalic Acid (PTA)
- MTBE
- Mono Ethylene Glycol (MEG)
- Ethylene Vinyl Acetate Copolymer (EVA)
- High Density Polyethylene (HDPE)
- Linear Alkyl Benzene (LAB)
- Linear Low Density Polyethylene (LLDPE)
- Diethyylene Glycol (DEG)
- Polypropelene Homopolymer (Homo PP)
- Polypropelene Copolymer (PPCP)
- Cycolopentene
- 1,3-Butadiene
- Benzene
Polypropelene Homopolymer (Homo PP)
Polypropylene Homopolymer (PPH) is a crystalline material is noted for its high strength-to-weight ratio, excellent chemical ressistance and high performance in thrmoforming and corrosive environment.
| PROPERTIES | SPECIFICATIONS |
|---|---|
| Density (g/cm3) | 0.905 |
| Surface Hardness | RR90 |
| Tensile Strength (MPa) | 33 |
| Flexural Modulus (GPa) | 1.5 |
| Notched Izod (kJ/m) | 0.07 |
| Linear Expansion (/°C x 10-5) | 10 |
| Elongation at Break (%) | 150 |
| Strain at Yield (%) | 10 |
| Max. Operating Temp. (°C) | 100 |
| Water Absorption (%) | 0.02 |
| Oxygen Index (%) | 17 |
| Flammability UL94 | HB |
| Volume Resistivity (log ohm.cm) | 17 |
| Dielectric Strength (MV/m) | 28 |
| Dissipation Factor 1kHz | 0.0001 |
| Dielectric Constant 1kHz | 2.28 |
| HDT @ 0.45 MPa (°C) | 105 |
| HDT @ 1.80 MPa (°C) | 65 |
| Material. Drying hrs @ (°C) | NA |
| Melting Temp. Range (°C) | 210-290 |
| Mould Shrinkage (%) | 1.5 |
| Mould Temp. Range (°C) | 20-60 |
Orthotic and prosthetic devices
Plating and anodizing process equipment
Plenums and manifolds
Pump components
Secondary containment
Storage tanks
Valve bodies
Metal finishing
Chemical processing and storage
Medical devices
Washers
Diethylene Glycol (DEG)