Energy
- Bitumen
- Fuels
- Other Refinery Products
- Petrochemicals
- Toluene
- Triethylene Glycol
- Polyvinyl Chloride (PVC)
- C5
- Purified Terepthalic Acid (PTA)
- MTBE
- Mono Ethylene Glycol (MEG)
- Ethylene Vinyl Acetate Copolymer (EVA)
- High Density Polyethylene (HDPE)
- Linear Alkyl Benzene (LAB)
- Linear Low Density Polyethylene (LLDPE)
- Diethyylene Glycol (DEG)
- Polypropelene Homopolymer (Homo PP)
- Polypropelene Copolymer (PPCP)
- Cycolopentene
- 1,3-Butadiene
- Benzene
Linear Low Density Polyethylene (LLDPE)
Very flexible, natural milky color, translucent with high impact strength. Excellent for mild and strong buffers, good chemical resistance. Good water vapor and alcohol barrier properties. Poor gas barrier, sterilizable with EtO or gamma radiation. Good stress crack and impact resistance.
| PROPERTIES | SPECIFICATIONS |
|---|---|
| Density (g/cm3) | 0.92 |
| Surface HardnessSD | 48 |
| Tensile Strength (MPa) | 20 |
| Flexural Modulus (GPa) | 0.35 |
| Notched Izod (kJ/m) | 1.06+ |
| Linear Expansion (/°C x 10 5) | 20 |
| Elongation at Break (%) | 500 |
| Strain at Yield (%) | 20 |
| Max. Operating Temp. (°C) | 50 |
| Water Absorption (%) | 0.01 |
| Oxygen Index (%) | 17 |
| Flammability UL94 | HB |
| Volume Resistivity (log ohm.cm) | 16 |
| Dielectric Strength (MV/m) | 25 |
| Dissipation Factor 1kHz | 0.0003 |
| Dielectric Constant 1kHz | 2.3 |
| HDT @ 0.45 MPa (°C) | 45 |
| HDT @ 1.80 MPa (°C) | 37 |
| Material. Drying hrs @ (°C) | NA |
| Melting Temp. Range (°C) | 220-260 |
| Mould Shrinkage (%) | 3 |
| Mould Temp. Range (°C) | 20 – 60 |
| FILM | Packaging, particularly film for bags and sheets |
| ROTO MOLDING | Water Storage Tanks, Chemical Tanks, Garbage Bins |
| LAMINATION | woven bags, Al – foil, Jute & Paper |
| INJECTION MOULDING | toys, lids, buckets and containers, pipe |